Hermetic plastic molded mems device package and method of fabrication

ABSTRACT

A hermetically packaged microelectromechanical system (MEMS) device has a substrate with an assembly pad ( 101 ) and a plurality of terminals ( 102 ); a chip ( 110 ) with a MEMS mechanical element ( 111 ) of a first height ( 111   a ) assembled on the pad and connected to the terminals by wires ( 120 ) with an insulating coat ( 121 ); a ridge ( 130 ) on the substrate, which surrounds the MEMS element ( 111 ) with a second height ( 130   c ) greater than the first height and comprises a plastic compound ( 131 ) filled with particles ( 132 ) and a surface ( 130   a,    130   b ) having an adhering moisture-impermeable seal layer ( 133 ); and a moisture-impervious lid ( 140 ) attached to the ridge by moisture-proof bonds ( 150, 151 ), sealing the volume ( 160 ) enclosed by the lid, the chip, and the metalized ridge as a hermetic space for the MEMS element ( 111 ).

This application is a divisional of U.S. Non Provisional application Ser. No. 13/914,013 filed Jun. 10, 2013, which claims the benefit of U.S. Provisional Application No. 61/657,355 filed Jun. 8, 2012, the entirety of both are incorporated herein by reference.

BACKGROUND

This relates to semiconductor devices and processes, and more specifically to the structure and fabrication of hermetic plastic packages for microelectromechanical system (MEMS) devices.

The wide variety of products collectively called micro-electromechanical system (MEMS) devices are small, lightweight devices on the micrometer to millimeter scale, which may have mechanically moving parts and often movable electrical power supplies and controls, or they may have parts sensitive to thermal, acoustic, or optical energy. MEMS devices have been developed to sense mechanical, thermal, chemical, radiant, magnetic, and biological quantities and inputs, and produce signals as outputs. Because of the moving and sensitive parts, MEMS devices have a need for physical and atmospheric protection. Therefore, MEMS devices are supported on a substrate and surrounded by a housing or package, to shield the MEMS components against ambient and electrical disturbances, and against stress.

A MEMS device integrates mechanical elements, sensors, actuators, and electronics on a common substrate. The manufacturing approach for a MEMS device aims at using batch fabrication techniques similar to those used for other microelectronics devices. Such devices can thus benefit from mass production and minimized material consumption to lower the manufacturing cost, while trying to exploit the well-controlled integrated circuit technology.

Example MEMS devices include mechanical sensors, both pressure sensors including microphone membranes, and inertial sensors such as accelerometers coupled with the integrated electronic circuit of the chip. The mechanically moving parts of a MEMS devices are fabricated together with the sensors and actuators in the process flow of the electronic integrated circuit (IC) on a semiconductor chip. The mechanically moving parts may be produced by an undercutting etch at some step during the IC fabrication. Examples of specific bulk micromachining processes employed in MEMS sensor production to create the movable elements and the cavities for their movements are anisotropic wet etching and deep reactive ion etching.

MEMS device packages do not generally have to be hermetic, i.e., impermeable to water molecules. Consequently, typical MEMS devices may use sealants made of polymeric compounds. Some MEMS devices do, however, require hermetic packages. Example of devices requiring hermetic packages include digital micromirror devices (DMDs), such as the DLP® DMD devices available from Texas Instruments. A typical DMD includes an array of individually addressable light modulating pixel element micromirrors, the reflectors of each of which are selectively positioned to reflect or not to reflect light to a desired site.

Conventional hermetic packaging of MEMS devices usually involves a packaging process that departs from the processes normally used for non-MEMS device packaging. MEMS hermetic packaging is expensive not only because the package often includes a ceramic material, or a metallic or glass lid, but also because the package must be configured to avoid contact with moving and other sensitive parts of the MEMS device and to further allow a controlled or reduced atmosphere inside the package. The high package cost is, however, in conflict with market requirements for many applications of MEMS devices, which put a premium at low device cost and, therefore, low package cost. Further, the conventional fabrication of hermetic MEMS packages also encounters many technical challenges, such as those caused by potentially high temperatures in connection with welding of a hermetic lid to the package base. As an example, a recently proposed package with a sealing process using a glass core involves temperatures considerably above 450° C., typically between 525 and 625° C. dependent on the sealing glass selected. These temperature ranges are a risk for the reliability of silicon integrated circuits and for proper functioning of many MEMS device components.

There is a need for low cost hermetic packaging of MEMS devices.

SUMMARY

Structures and processes are disclosed for hermetically sealed microelectromechanical systems (MEMS) devices.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view of an example embodiment of a hermetically packaged microelectromechanical system (MEMS) device.

FIGS. 2A and 2B are cross-sectional views of other example embodiments of hermetically packaged MEMS devices.

FIGS. 3-9 illustrate steps in example methods for fabricating hermetic MEMS device packages.

DETAILED DESCRIPTION OF EXAMPLE EMBODIMENTS

FIG. 1 illustrates an example embodiment of a hermetically packaged microelectromechanical system (MEMS) device 100.

Device 100 has a metallic leadframe substrate comprising a pad 101 and leads 102. A semiconductor chip 110 is attached to leadframe pad 101. Chip 110 may be an integrated circuit die chip that includes MEMS micromechanical components 111 which extend to a first height 111 a above an upper surface of the chip. The components 111 may, for example, be movable micromechanical elements such as position-settable mirrors of a digital micromirror device (DMD). Chip 110 may be made of silicon, silicon germanium, gallium arsenide, III-V compounds, or any other material used in integrated circuit or microelectronic technology. Chip 110 may be used without backgrinding (between about 0.4 and 0.9 mm thick). Chip 110 has a plurality of bondable terminal pads 112. The terminal pads 112 may be metal such as aluminum or copper, or any other material to which conductive connectors may be affixed. Pads 112 are connected to respective leads 102 by metallic bonding wires 120, which may be coated with an insulating layer 121.

The substrate may be a metal leadframe, as shown in FIG. 1, or a multimetal-level substrate, laminated substrate, or any other suitable support structure, as shown in FIGS. 2A and 2B. When the substrate is a leadframe, the metal is preferably copper or a copper alloy. Alternative metal selections include aluminum, iron-nickel alloys, and Kovar™ material. One or more surfaces 101 a of the leadframe may be prepared to facilitate solder attachment, for instance by a sequence of plated layers of nickel, palladium, and gold. In addition, the one or more surfaces may have a metal layer deposited to enhance thermal conductivity, for instance by a plated layer of silver. Preferred thickness of the leadframe metal for the example embodiment shown in FIG. 1 is 0.2 mm; other embodiments may use thinner or thicker (e.g. 0.5 mm) leadframe metal. From the standpoint of low cost and batch processing, it is preferred to start with a strip of flat sheet of metal and fabricate pad and leads by stamping or etching. Pad 101 may stay in the plane of the flat sheet, or it may be offset for facilitating assembly and wire bonding processes. Leads 102 may retain the flatness of the sheet, as in QFN and SON packages, or they may be formed as cantilever leads with spring-like characteristics. The assembly and packaging process flow is concluded by singulating the strip into discrete units.

As FIG. 1 depicts, bonding wires 120 span the distance from chip terminals 111 to respective substrate leads 102 in some sort of arc. In the example of FIG. 1, ball bonding is used; alternatively double-stitch bonding or ribbon bonding may be employed. The conventionally preferred gold wires are recently more and more replaced by wires made of lower cost metals such as copper or aluminum. The common trend is to miniaturize the distance between adjacent wire arcs by selecting a finer pitch center-to-center of the chip bond pads (for instance from 70 μm to 35 μm) and reducing the diameter of the wires (for instance from 30 μm to 20 μm). The miniaturization trend continues in spite of the fact the stiffness of the bonded wires and thus the robustness of the wire spans are decreased, even for specially alloyed or heat treated wires. For example, the stiffness of 20 μm and 15 μm diameter wires is 41% and 13%, respectively, of a 25 μm diameter wire.

FIG. 1 shows that the surfaces of the wire arcs may be coated with a layer of a heterocyclic compound; the coating layers are designated 121. After completing the wire-bonding operation proper, automated bonders (for example, like those available from Kulicke & Soffa, Fort Washington, Pa.) offer on-bonder dispense systems which allow the dispensing of liquids over just-completed wire spans. An example liquid consists of a solution of about 1 millimole per liter (mmol/L) of a heterocyclic compound in ethanol. In the dispensing step, a layer of liquid is formed on the wire surfaces. The ethanol will be evaporated after dispensing, while at least one monolayer 121 of the heterocyclic compound remains adsorbed on the wire surfaces. The adsorbed layer 121 is shown in the insert of FIG. 4 by the enlargement of a wire portion 120 a. The preferred heterocyclic compound is imidazole; after being adsorbed on the surfaces of wire 120, imidazole can act as catalyst for polymerizing epoxy-type long-chain molecules.

As the example embodiment of FIG. 1 illustrates, the substrate, exemplified by the leadframe with pad 101 and leads 102, has a ridge 130 formed by a plastic compound 131 filled with particles 132 and covered on its surface by a metalized layer 133. Preferred choices for compound 131 include a polymerizable epoxy-based resin and silicone. Compound 131 provides the supporting body of the package for device 100 by connecting pad 101 and leads 102 and defining the shape of the device package. Compound 131 forms the ridge 130 so that the ridge fully surrounds the MEMS elements and has a slope 130 a extending from ridge top 130 b towards the MEMS elements. Top 130 b of the ridge has a second height 130 c relative to chip surface 110. Second height 130 c is greater than the first height 111 a. Slope 130 a may be quite steep, but preferably is less inclined than vertical. Furthermore, compound 131 encloses the wires 120.

The filler particles 132 of plastic compound 131 may be electrically insulating or electrically conductive. As for insulating fillers, preferred materials include particles of silicon dioxide and silicon carbide. As for conductive fillers, preferred materials include particles made of metals such as silver and copper, and of compounds such as nickel-graphite and carbon fibers. When conductive fillers are employed, wire insulations 121 are preferably used. The percent of filler particles 132 in a volume of compound 131 may vary widely; the volume content of insulating fillers may reach between 80% and >90%. A suitable method of applying the compounds is transfer molding; alternative methods are becoming popular in the semiconductor industry. Preferably, the filler particles have a diameter of about 1 to 10 μm and are preferably approximately spherical, since particles with sharp corners may be abrasive to the precision steel surfaces and gates of molding equipment.

On the surface 130 a and 130 b of the ridge is a metallized layer 133, the ends of which are sealed to chip metal ring 113 surrounding the MEMS; layer 133 can be manufactured by several methods. In one method, the whole surface of the ridge 130, including slope 130 a, is activated by etching the surface in a concentrated acid, which roughens the ridge surface but does not attack the resist protecting the MEMS at this stage of the packaging process flow. In another activation method, the ridge surface is activated by ion bombardment or by exposure to a plasma discharge. After one of these activation steps and without delay, a layer of metal, such as palladium, is deposited, preferably by plating, on the activated surface. The resulting metal layer is impervious to moisture and adheres to the compound surface.

An alternative method for forming a metalized layer 133 on the ridge surface uses a deformable seal film. Preferably, this film includes a foil of polyimide between about 5 μm and 10 μm thick laminated with an adhering metal foil, also between about 5 μm and 10 μm thick. The seal film lines the surface of ridge top 130 b and slope 130 a, but is non-adhering to the steel mold employed for the molding step (see below).

The example embodiment of FIG. 1 further exhibits a moisture-impervious lid 140. For MEMS device 100, lid 140 is flat, parallel to the orientation of the MEMS, and transparent to visible light; a suitable lid is made of glass. In other embodiments, lid 140 may be made of silicon transmissible to infrared wavelengths. For still other embodiments, lid 140 may be dome-shaped. In all examples, lid 140 is attached to the metalized layer 113 on ridge top 130 b by moisture-proof bonds. Preferred bonds may include a layer 150 of metal and a layer 151 of intermetallic compounds. An example of fabricating such preferred moisture-proof bonds is described below.

Depending on the thickness of lid 140, the overall thickness 190 of example device 100, especially as a package for digital micromirror devices (DMDs), may be in the range from about 1.5 mm to 3.0 mm. Examples of lateral dimensions for device 100 in FIG. 1 are about 14 mm as length 191 and about 5 mm as width (not shown in FIG. 1).

As a result of the structure and materials of the package shown in FIG. 1, the volume 160 enclosed by lid 140, chip 110, and metalized ridge 130 a and 130 b is sealed as a hermetic space for MEMS components 111.

FIGS. 2A and 2B illustrate other example embodiments of a sealed volume suitable as hermetic space for MEMS components, wherein the embodiments are based on metal/insulator laminated or tape substrates, which offer greatly increased numbers of input/output terminals compared to leadframe-based devices. In both examples, the hermetic volume is enclosed by a chip, a lid, and a metalized plastic ridge; the ridge rests on the metal/insulator laminated or tape substrate.

For packaged MEMS device 200 depicted in FIG. 2A, the hermetic space 260 is constructed analogous to the space 160 of FIG. 1: The substrate 201, in FIG. 2A based on laminate or tape, has an assembly pad and a plurality of terminals 202. A chip 210 with MEMS movable elements 211 extending to a first height 211 a above the chip surface is assembled on the pad and connected to the terminals by wires 220 with an insulating coat 221. Attached to the substrate is a ridge 230, which surrounds the movable elements and has a second height 230 c (for instance, between about 0.15 and 0.3 mm) measured from the chip surface, greater than the first height. The ridge comprises a plastic compound 231 filled with particles 232, which may be electrically insulating or conductive. The surface 230 a, 230 b of the ridge is metalized. It may have a plated layer of metal, or may have an adhering moisture-impermeable seal film 233. A moisture-impervious lid 240 is attached to the ridge by moisture-proof bonds 250, 251, sealing the volume 260 enclosed by the lid, the chip, and the metalized ridge as a hermetic space for the MEMS elements.

FIG. 2B illustrates another example embodiment based on a metal-insulator laminate or tape. The embodiment features two separate sealed cavities 270 and 271; one cavity may be suitable as a hermetic space for MEMS movable components 213, and the other cavity may be a hermetic space for another component such as a stack of chips, a sensor, and a passive component. As FIG. 2B shows, both spaces together are enclosed by a common chip 280 and a common lid 240, and a plurality of plastic ridges 230 and 234 with metalized surfaces.

FIGS. 3-9 illustrate steps in an example process for fabricating hermetic plastic molded MEMS packages using leadframe-based substrates. It should be stressed, however, that analogous process steps are applicable to packages using substrates based on laminates or tapes. FIG. 10 displays a process step for a device using a laminate- or tape-based substrate.

In FIG. 3, a strip of leadframes is placed on a heatable work plate. Alternatively, the leadframe strip may be placed on a laminated tape 103 to protect against mold bleeding and plating damage in later process steps. FIG. 3 depicts a leadframe of the strip, including chip attachment pad 101 and a plurality of leads 102. A chip 110 is attached, for instance by an adhesive epoxy, to pad 101. Chip 110 includes MEMS movable elements 111, which at this stage are supported by protective material 114. An example of protective material is a layer of photoresist. Chip 110 further includes a plurality of metallic terminals 112 and, for certain MEMS devices, a metallic ring 113 surrounding the MEMS elements.

FIG. 3 illustrates the process step of connecting the chip terminals 112 with the leadframe leads 102 by bonding wires 120. A preferred connecting method is ball bonding, which spans the wire in an arc between terminal and lead. When the later encapsulation step will use a polymeric compound with electrically conducting fillers, the bonding wires are preferably surrounded with an electrically insulating skin right after the bonding step. Further details of such a method are disclosed in U.S. application Ser. No. 13/787,198, filed 6 Mar. 2013, the entirety of which is incorporated herein by reference.

As mentioned above, automated bonders offer on-bonder dispense systems which allow the dispensing of liquids over just-completed wire spans. An example liquid consists of a solution of about 1 millimole per liter (mmol/L) of a heterocyclic compound in ethanol. In the dispensing step, a layer of liquid is formed on the wire surfaces. The ethanol will be evaporated after dispensing, while at least one monolayer 121 of the heterocyclic compound remains adsorbed on the wire surfaces. The preferred heterocyclic compound is imidazole (see inset of FIG. 4); after being adsorbed on the surfaces of wire 120, imidazole can act as catalyst for polymerizing epoxy-type long-chain molecules.

By way of explanation, a heterocyclic compound has a five-membered ring, which includes besides carbon atoms other atoms such as nitrogen, oxygen, or sulfur. The heterocyclic compounds preferred for this process step have at least one nitrogen atom. The basic compound is pyrrole (C₄H₅N₁) with a five-membered di-unsaturated ring and one nitrogen atom. Pyrazole (C₃H₄N₂) has two adjacent nitrogen atoms as part of the ring. Isomeric with pyrazole is imidazole (C₃H₄N₂), which has two non-adjacent nitrogen atoms as part of the ring. As catalyst, imidazole is the preferred compound for the present process step (see inset of FIG. 4). An alternative to the preferred imidazole is triazole (C₂H₃N₃), containing a five-membered ring with three nitrogen atoms as part of the ring.

Next process steps are summarized in FIG. 4. The leadframe together with the attached and wire-bonded chip, with the layers 121 of heterocyclic compound adsorbed on the wire surfaces, is loaded into the cavity 402 of a steel mold suitable for the transfer molding process flow. The mold consists of a top half 401 a and a bottom half 401 b. The top half 401 a has been designed to create on the substrate (leadframe) a ridge (designated 130 in FIG. 1) surrounding the MEMS and having a height greater than the height of the MEMS elements. Both mold halves are preheated to a temperature between ambient temperature and the liquefying temperature of the pellet. After placing the assembly on the bottom half 401 b of the cavity, the top mold half 401 a is closed, whereby the preheated cavity 401 is connected by a preheated runner 403 with the preheated pressure chamber 404.

Solid pellets 410 of the packaging compound 131 are then loaded into the preheated pressure chamber 404. The number of pellets may vary according to the number of cavities to be filled by the transfer step. The top pellet is weighed down by movable plunger 405, which can be activated to pressure the packaging material into the cavity after liquefying the pellets.

In a preferred packaging material for transfer-molded devices, each pellet is composed of an epoxy-type resin, or another suitable thermoset compound, and about 80 to 90 weight % filler grains 132. For electrically insulating fillers, preferred materials include particles of silica, silicon dioxide silicon carbide, alumina trihydrate, and glass fibers. For electrically conductive filers, preferred materials include particles made of metals such as silver and copper, and of compounds such as nickel-graphite and carbon. In addition, molding compounds may also include coupling agents, hardeners, flame retardants, mold release agents, and curing agents to convert the resin into a cross linked (polymerized) structure.

The preheating time for conventional molds is about 40 s. After solid pellets 410 have been loaded into pressure chamber 404, the temperature of the chamber is increased to reach the temperature of low viscosity (liquefying) of the resin, preferably 175° C. The time interval needed to raise the temperature of the solid pellets 410 to the liquefying temperature is preferably between about 5 s and 6 s, dependent on the mold employed; in automolds, the time is between about 2 s and 3 s. The transfer to cavity 402 of the liquefied resin takes about 18 s to 30 s in conventional molds, dependent on the transfer speed, and about 8 s to 10 s in automolds (at 3 mm/s transfer speed). During the time interval (melting time plus transfer time), the vapor 411 of the resin molecules can spread during melting time and be pushed during transfer time from chamber 410 through runner 403 to cavity 402, where the vapor distributes throughout the cavity, reaching the semiconductor assembly inside the cavity, where the assembly includes the bonding wires with the surfaces covered by the adsorbed heterocyclic compound molecules.

When the resin molecules arrive in cavity 402 and reach the wires with the surfaces covered by the adsorbed heterocyclic compound molecules, the resin molecules are cross-linked into at least a monolayer 121 of polymeric structure on the wire surfaces, whereby the adsorbed heterocyclic compound molecules act as catalysts. For most molds, the time interval and the polymerization speed are sufficient to form a layer of polymerized molecules on the wire surfaces with an effective thickness of several monolayers. The insulating characteristic of the polymerized layer is enhanced by the insulating quality of the surface coating with catalyst heterocyclic molecules.

The semi-viscous polymeric resin progresses controlled in a steady wave front until cavity 402 is completely filled with resin. Supported by the curing agent, the resin is allowed to partially polymerize in the cavity while the temperature of the mold is lowered so that the cavity can be opened by lifting the top mold half 401 a. After allowing the temperature to cool further, the encapsulated assembly can be removed from the cavity. FIG. 5 illustrates the device at this stage.

In a next process step, the surfaces 130 a and 130 b of the molded ridge 130 are metalized by one of several methods. In the first phase, the ridge surface may be activated, for instance by etching the surface in a concentrated acid, which roughens the ridge surface but does not attack the resist 114 protecting the MEMS elements 111, or by bombarding the surface with ions or exposing is to a plasma discharge. As FIG. 6 indicates, after one of these activation steps and without delay, a seed layer 133 a of metal, such as palladium or tin, is deposited, preferably by plating, on the activated surface. Then, a layer 133 b of electroless nickel or electroless copper is plated, followed by a layer 133 c if electrolytic copper. The resulting metal layer 133 is impervious to moisture, adheres to the compound surface 130 a and 130 b, and is sealed in contact with chip metal ring 113. The metal of layer 133 is referred to herein as first metal.

Alternatively, the metallization of the plastic surface can be combined with the molding process; this alternative method is depicted in FIG. 7. The transfer molding process step depicted in FIG. 7 employs a deformable seal film 701 on the inner wall of the top mold 401 a. Preferably, this film includes a plastic foil, preferably made of polyimide, between about 5 μm and 10 μm thick laminated with an adhering metal foil, also between about 5 μm and 10 μm thick. Preferred metals include noble metals such as palladium and silver; other suitable choices include copper, nickel, tin and other metals and compounds with no or very low oxidation tendency. Film 701 is oriented so that the plastic foil faces the device and the metal foil faces the top mold half Since the metal of seal film takes the place of the deposited metal layer discussed in the previous method, this metal of the foil is also referred to herein as first metal.

The top half 401 a of the mold has been designed to create on the substrate (leadframe) a ridge (designated 130 in FIG. 1) surrounding the MEMS elements and having a height greater than the height of the MEMS elements. As FIG. 7 shows, seal film 701 is stretched continuously between the reels 710 and lines the complete inner surface of mold top 401 a. However, seal film 701 is non-adhering to the steel of the top mold. On the other hand, seal film 701 will be adhering to the particle-filled resin of the molding compound. As shown in FIG. 4, the cavity of the mold, loaded with the chip assembled on the substrate, is connected by a runner with the chamber of the mold for the molding compounds.

The next process steps are analogous to the steps depicted in FIG. 4. The heated pressure chamber of the mold is loaded with a solid pellet of a packaging compound including a polymerizable resin and filler particles. The mold is closed and the compound is pressured through the runner into the mold cavity, where it progresses as a controlled front through the cavity. On its way, the compound encapsulates the wires 120, forms the ridge 130, and adhesively contacts the seal film 701.

In the next process step, the mold is opened, whereby the top half 401 a is separated from the seal film 701, which continues to adhere to the surfaces 130 a and 130 b of ridge 130. Thereafter, the seal film 701 is patterned by removing (preferably with an etching technique) any excess film portions beyond the ridge top 130 b, including the portions remote from the MEMS elements as well as the portions 701 a encapsulating the protective material 114 of the MEMS elements. The metal foil of film 701 remains in contact with metal ring 113 surrounding the MEMS elements.

In next process steps, summarized in FIG. 8, the protective material 114 (for instance photoresist), which was shielding MEMS elements 111 throughout preceding process steps, is removed, thus releasing the elements, and some getter or lube material 801 may be dispensed in the proximity of the elements.

FIG. 9 illustrates the process steps of the liquid phase method. A stripe 150 of a layer made of a second metal is deposited onto the metalized layer 133 on the ridge top; as discussed above, the ridge top of covered with a layer 133 of a first metal. The stripe is configured to surround the MEMS micromechanical elements 111 at a distance and has a width; the second metal is selected from a group including gold, silver, and tin, and titanium.

Next, a lid 140 is provided, which is impervious to water molecules and has a size sufficient to cover the second metal stripe and the area surrounded by the second metal stripe; the lid can thus function as a cover for the MEMS device. Lid 140 may be shaped as a flat plate with a thickness between about 0.4 and 0.7 mm, as shown in FIG. 9, or it may be shaped as a dome or any other configuration as a cover for the MEMS device. Dependent on the type and functionality of the MEMS device, lid 140 may be selected from a group including glass, quartz, and silicon, and a plurality of metals and ceramics. Glass is particularly appropriate for DMD-type MEMS device.

In the next process step, a layer 151 of a third metal is deposited on the lid surface facing the ridge; the third metal layer is configured as a stripe matching the outline of the second metal stripe, but preferably has a width smaller than the width of the second metal stripe. The third metal is selected from a group including indium, gold and copper. The intent is to form, together with a selected second metal, binary systems such as indium/gold; gold/tin; copper/tin, and indium/tin. These binary systems form their first eutectic at a relatively low temperature, while the resulting intermetallic compounds need a considerably higher temperature for re-melting.

In the next process step, the lid and the substrate are aligned to bring the third metal layer into contact with the second metal layer along the entire stripe. Then thermal energy is applied to dissolve the third metal into the second metal layer and form intermetallic compounds adhering the lid and the ridge and establishing a hermetic bond. In a favored binary combination, the second metal is gold as a representative of metals with a melting temperature >400° C. and the third metal is indium as a representative of metals with a melting temperature <260° C., while the gold-indium intermetallic compounds have a melting temperature >400° C. Details of using this binary combination, favored for bonding at low melting temperature and reflowing at high temperature, are disclosed in U.S. application Ser. No. 13/67,734, filed 8 Nov. 2012, and U.S. application Ser. No. 13/840,688, filed 15 Mar. 2013, the entireties of both of which are incorporated herein by reference.

With the metallic bond between layers 150 and 151 completed, the volume enclosed by lid 140, chip 110, and metalized ridge 130 is sealed as a hermetic space 160 for the MEMS mechanical elements 111. As mentioned above in conjunction with FIGS. 2A and 2B, an analogous hermetic space can be reached for devices with substrates based on laminates or tapes, instead of leadframe-based substrates. When substrates are applied in strip form for batch processing, the final process step includes singulation of discrete units.

The substrate material used for supporting the MEMS mechanical elements may include any material that is usable for circuit components in integrated circuit manufacture. This includes a variety of semiconductor components, as well as a variety of non-semiconductor components.

For some MEMS devices, the metallization of the plastic ridge may be supported, when the fillers of the plastic resin are not randomly distributed, but exhibit a preference of orientation. Such imposed orientation may be achieved by an outside magnetic field, when at least a subset of the fillers is made of magnetically responding materials. The bonding wires may be electrically insulated by using skins made of polymeric sheaths.

The bond of the lid to the metalized ridge may be formed by intermetallic compounds of binary metal systems, or by intermetallic compounds of ternary or higher metal systems.

Those skilled in the art will appreciate that many other modifications may be made to the described example embodiments, and also that many other embodiments are possible, within the scope of the claimed invention. 

What is claimed is:
 1. A hermetically packaged microelectromechanical system (MEMS) device comprising: a substrate having an assembly pad and a plurality of terminals; a chip assembled on the pad and connected to the terminals by wires having an insulating coat, the chip including a micromechanical element extending a first height above a chip surface; a ridge on the substrate, the ridge surrounding the micromechanical element, the ridge extending above the chip surface by a second height greater than the first height and comprising a plastic compound filled with electrically conductive particles and a ridge surface having an adhering moisture-impermeable seal layer; and a moisture-impervious lid attached to the ridge by moisture-proof bonds, sealing a volume defined by the lid, the chip, and the ridge.
 2. The device of claim 1, further including an insulating layer coating the connecting wires.
 3. The device of claim 1, wherein the substrate is a metallic leadframe including a chip assembly pad and a plurality of leads.
 4. The device of claim 1, wherein the substrate is a laminate of insulating and metallic levels. 